Magnesium oxide dispersions

ABSTRACT

MgO in combination with a rubber plasticizer and a surface active agent and/or metallic soap for use in chloroprene polymer compounding and processing.

United States Patent 1 Dalhuisen et a1.

[ 51 Feb. 20, 1973 Filed:

MAGNESIUM OXIDE DISPERSIONS Inventors: Albert J. Dalhuisen, Sunnyvale; William H. Deis, Belmont; David C. Burgett, Daly City, all of Calif.

Assignee: Merck & Co., Inc., Rahway, NJ.

Jan. 13, 1971 Appl. No.: 106,272

Related US. Application Data Continuation-in-part of Ser. Nos. 19,517, March 13, 1970, abandoned, and Ser. No. 78,300, Oct. 5, 1970, abandoned.

US. Cl ..260/23 H, 252/182, 252/309, 260/233, 260/23.7 H, 260/23.7 M, 260/27 BB, 260/285 A, 260/285 B, 260/30.6'R, 260/312 MR, 260/3l.8 DR, 260/336 AQ,

, 260/923, 260/887, 260/888 Int. Cl. .'.....C08d 9/02 Field ofSearch ..260l23.7 H,23.7 M,92.3,

260/3346 AQ, 23.3, 23 H; 252/309, 182

The Neoprenes by Murray et al., (1963), pgs. 21-31 and 39-41.

Neoprene Latex by Carl, (1962), pgs. 125-128. Gas lmpermeable Fabric Neoprene Coated by Du- Pont, (1944), 2 pages.

Hackhs Chemical Dictionary, page 777, (1944).

Primary Examiner-Donald E. Czaja Assistant Examiner-Donald J. Barrack Attorney-Julian S. Levitt, J. Jerome Behan and l.

Louis Wolk [57] ABSTRACT MgO in combination with a rubber plasticizer and a surface active agent and/or metallic soap for use in chloroprene polymer compounding and processing.

47 Claims, No Drawings MAGNESIUM OXIDE DISPERSIONS This application is a continuation-impart of U.S. patent application Ser. No. 19,517, filed Mar. 13, 1970 and U.S. patent application SerjNo. 78,300, filed Oct. 5, 1970 all now abandoned.

This invention relates to improvements in the processing of rubber materials. More particularly this invention is concerned with an improved form of magnesium oxide for use in regulating the scorch and cure rate of neoprene rubber formulations. In addition, the MgO material of this invention results in the production of neoprene vulcanizates of excellent quality.

Neoprene is the generic term applied to the group of synthetic elastomers based on the polymers of chloroprene (2-chloro-l,3-butadiene). The group of general purpose neoprene formulations includes broadly two classes, the sulfur-modified (for example, Type G Neoprene) and the nonsulfur-modified (for example, Type W Neoprene). It should be understood that this invention is applicable to all types of chloroprene polymers made by polymerization, for example, in the presence of mercaptans or other modifying (chain transfer) agents such as the dialkyl xanthogen disulfides, or in the presence of sulfur, followed by plasticizing treatment, or by very limited polymerization without agents followed by removal of the unchanged chloroprene monomer. All these processes are fully described in the prior art. See for example U.S. Pat. Nos. 1,950,436; 2,227,517; 2,234,215; and 2,567,117. Neoprene GNA is an example of a G type of neoprene. This particular neoprene is described and its method of manufacture is given at pages 769-771, Synthetic Rubber, edited by 6.8. Whitby, [John Wiley and Sons Inc. (1954)].

The polymers of chloroprene used include both polychloroprene itself and blends using a chloroprene polymer. Likewise, materials used with the chloroprene polymers as antioxidants, plasticizers, curing agents, accelerators, retarders, reinforcing agents, pigments and extenders are well known, as are the quantities which should be used under various circumstances. This prior art is applicable in the present invention.

The use of MgO in the processing of neoprene compounds is well-known. The mechanism by which MgO benefits the vulcanization process is not clearly understood, but the influence it exerts has been briefly described in Whitby Synthetic Rubber, (1954), pages 775-776 (John Wiley) as providing a balance between processing safety and cure rate when the MgO is combined with other oxides such as zinc oxide. The use of zinc oxide as the sole curing agent produces both a fast cure and a uniform state of cure on extended vulcanization; i.e., such stocks are flat curing. The limitations of such compounds include a pronounced tendency to be scorchy, or result in a premature curing of the system. In addition, there results a leveling off of cure at a relatively low point. The use of magnesia as the sole curing agent produces Neoprene compounds which are very slow curing and are safe processing, but in which curing activity tends to persist. In addition, magnesia improves vulcanizate aging properties, presumably by serving as acceptors for the minute amounts of hydrogen chloride which are released from the neoprene during processing, curing and vulcanizate aging. In combination, zinc oxide and magnesia supplement each other to produce wellbalanced stocks, the properties of which can be varied, frequently to advantage, by adjustment in the ratio of one oxide to the other.

It is the purpose of this'invention to provide a highly reactive MgO preparation for neoprene processing which disperses rapidly and uniformly in the neoprene. The MgO dispersions of this invention, when employed in the processing of neoprene, result in improved Mooney Scorch protection (original and after aging of the unvulcanized compound), and provide improved processing and storage safety of unvulcanized neoprene. Furthennore, the dispersion has no adverse effect on the vulcanizate properties of neoprene. This results in less scrap and allows more latitude and flexibility in the processing and storage of the unvulcanized neoprene. This highly active, readily dispersible MgO formulation is composed of magnesium oxide andat least one surface active agent and/or metallic soap and at least one rubber plasticizer.

MgO is currently employed in both powder and specified dispersed form for use in neoprene processing. However, the MgO dispersions of the invention result in the preparation of products with improved performance regarding Mooney Scorch Protection (original and after aging) when compared with the MgO preparations that are employed at this time in the rubber industry. The MgO dispersions of this invention may be utilized in either the liquid or solid state in the processing of neoprene. For example, the dispersions may be supplied to the neoprene manufacturer in the form of a paste, stick, block or pellet, etc in order that the dispersions may be conveniently utilized in the processing of neoprene. The particular form of the M g0 dispersion involves a matter of choice and may be prepared using conventional procedures well known to the art.

It is well known in the industry'that MgO, upon exposure to atmospheric moisture and carbon dioxide, is rapidly converted to the carbonate or hydroxide. However, neither magnesium carbonate nor magnesium hydroxide are effective in neoprene vulcanization in the manner in which MgO is effective. Accordingly, care must be continuously exercised to insure that the MgO preparation destined for use in neoprene processing does not experience a loss in activity. Another advantage of the dispersions of the invention relates to its ability to maintain the activity of the MgO over considerable periods of storage without employing the precautions normally confronting the industry.

This invention contemplates utilizing the neoprene grades" of MgO which are precipitated and calcined after precipitation. In addition to these light calcined, highly surface active forms of MgO, less active types of MgO may also be employed in the practice of this invention. Included within this class of less active MgO materials are heavy calcined types of MgO.

The amount of surface active agent and/or metallic soap to be employed in not critical and highly effective processing agents may be obtained utilizing 2.5 to 50 parts by weight of this material per parts by weight of MgO. The preferred range may vary from 5 to 15 parts per 100 parts by weight of MgO. It should be noted that the system may contain only a single surface active agent or mixtures thereof or only a metallic soap or mixtures thereof.

In addition members of both classes of materials may be combined with each other in order to obtain the operative amount of surface active agent and/or metallic soap. In other words, the amount of surface active agent and metallic soap may each vary within the range of percent through 100 percent with relation to the other.

The amount of MgO-surface active agent/metallic soap and rubber plasticizer to be employed in the processing of neoprene will usually vary from about 2 to 16 parts by weight per hundred parts of rubber. This will include systems where MgO is used as a processing material both with and without the presence of other metallic oxides. For most applications, the recommended level is 4 phr. 4

In the practice of this invention a plasticizer to rubber is utilized in combination with the MgO and surface active agent and/or metallic soap. The amount of plasticizer to be employed is not critical and may vary from about 5 to 70 parts per hundred parts of MgO. It should be noted that the system may contain either a single plasticizer or mixtures of different plasticizers.

The particular rubber plasticizer that may be employed in the practice of this invention is not critical and includes those plasticizers that are well known and conventionally employed for this purpose by the skilled artisans of the rubber art. In this regard see Morton, Introduction to Rubber Technology, pages 151-171, Reinhold Pubi. Comp. (1964); Murray and Thompson, The Neoprenes, pages 39-41, DuPont (1963); the plasticizers disclosed therein being incorporated by reference. Included among this class are:

Petroleum Oils, such as paraffmic, naphthenic, and aromatic.

Resin, waxes, and asphalt derived from petroleum oil are also encompassed within this class. Also included are mineral oils;

Esters, such as esters of organic alcohols and polybasic acids;

Resins and polymers, such as aromatic hydrocarbon resins and liquid elastomers, (e.g., polyisobutylene and polybutene);

Oils, pitch and resins obtained from pine trees and coal tar.

Natural fats and oils (vegetable oils, blown oils, fatty acids).

Coumarone indene resins (aromatic and aliphatic aromatic oils such as Bearflex LPO (Golden Bear Oil Company) and Califlux 550 (Golden Bear Oil Company). The esters are exemplified by butyl oleate, dibutylphthalate, and tricresyl phosphate, dioctyl sebacate, trioctyl phosphate and triethylene glycol caprylate. Illustrative of the resins and polymers are Kenflex N, (aromatic hydrocarbon) BRC-22, Para-Flux, Vistanex LM-MH (a non-staining polyisobutylene with a viscosity average molecular weight (staudinger) of 10,000

1 1,700) and the Flosbrenes Fluid SBR polymers which are liquid or fluid copolymers of styrene and butadiene containing approximately percent bound styrene. Of particular interest in this class is Flosbrene 25 MV which has a molecular weight of approximately 5,000

25 and a viscosity in poises of 4,500 (77 F.) and 550 (113 F.) [The Flosbrenes Fluid SBR Polymers, A.G. Susie and FJ. Sackfield, American Synthetic Rubber Corp.]. Examples of coumarone indene resinswhich may be employed in the practice of the invention include the Picco resins which are a family of petroleum derived polyindene or coumarone indene type resins. Of particular interest is Picco 6100-1-rand Piccotex 100 (alphamethylstyrene vinyltoluene copolymer) (molar ratio of l-alphamethylstyrene to 3-vinyltoluene) [Resins in Rubber, supra, pages 72-75, 86 and Product Data Sheet O79, Pennsylvania Chemical Corp., page 6]. Illustrative of vegetable oils which may be employed in the compounding of chloroprene polymers are linseed oil, rapeseed oil and safflower oil.

The polybutenes are a series of synthetic hydrocarbon polymers obtained by catalytic polymerization of normal and branched chained butenes. They are pale colored liquids of moderate to high viscosity and tackiness. Representative of the class of polybutenes useful in the practice of the invention are the Oronite polybutenes [New Improved Oronite Polybutenes, (1963), California Chemical Corp.]. Of particular interest is Polybutene No. 128.

No. 8 No. 16 N0. 18 N0. 20 N0. 24 N0. 32X No. 32

Test method No. 6 N0. 122 N0. 8

Physical properties:

Condition Visual Clear, bright and free from sediment or suspended matter Color, Gardner AS'IM D-1544 1 l 1 1 1 1 1 1 Specific gravity at /fi0 F AS'IM D-287 0.846 0.862 0. 880 0.888 0. 891 0. 898 0.905 0. 908 0.915 0. 917 Number average molecular weight Meehrolab osmometer SM-ISO-fi 330 440 040 730 800 950 1, 260 1, 400 50 700 Molecular weight dispersion index SM-lSO-fi 1.0 1.5 1. 6 1. 8 3 Viscosity at F., SSU AS'IM D445 and D-446 134 560 5, 700 9, 500 16, 500 40, 000 104, )00 123, 000 715, 000 890, 000 Viscosity at 210F., SSU ASIM D-445 and D446 41 63 250 350 550 1, 050 2, 460 2, 990 15, 800 19, 500 Viscosity index- ASTM D 567 66 87 90 103 105 112 116 118 122 122 Flash point, F ASTM D-92 270 280 335 335 370 400 485 435 500 510 Fire point, F ASTM D-92 295 320 390 415 430 470 560 520 605 615 Your point, F ASIM D-97 60 30 -10 +5 +10 +20 +35 +40 +55 +05 Loss of heating, percent (6 Hours at 329 F) ASTM D-fi 7. 6 1.0 0. 3 0. 4 0.1 Coeihcient of thermal expansion per C. 100 C.) SM-15-23 0.00079 0.00078 0.00074 0.00072 0.00072 0.00070 0. 00067 0. 00056 0.00063 0-0006 Chemical properties:

Bromine number, g./100 g SM-20-28 44 37 26 24 22 18 14 13 8 7 Neutralization value, mg.

kOH/i! AS'IM l)664 0.01 0. 01 0.01 0. 01 0.01 0.01 l). 01 0. 01 0.01 0. 0 Organic chloride as chlorine,

weight percent SM- 205 -12 0. 007 0. 004 0. 003 0. 003 O. 003 0. 003 0. 003 0. 003 0. 002 0. 002

Table Continued Test method No.0 No. a No. 10 No. 18 No. 20 No. 24 No. 32X No.32 N0. 122 N0. 128

Inorganic chlorides and sulfates ASTM D-878 None None None None None None None None None None Total sulfur, percent ASTM D-1552 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 Carbon residue, percenL ASTM D-189 None None None N one None None None None None None Water content, p.p.m ASTM D-1533 40 40 40 40 40 40 40 40 40 40 As indicated above, mixtures of various plasticizers Gravity, API 26.l

l e v e may be employed in the pract1ce of the 1nvent1on 1n adlo ggf f ggfigg 9222 dition to a single member. it has been found that desira- Cob, ASTM ble results are obtained when mixtures are employed, g fq hf- -ffi 420 particularly when one of the members of the plasticizer gi'z a'y m mixture is either a liquid elastomer such as polyisobu- Neutralization No. mg. KOH/g 0.03 tylene, polybutene or the Flosbrenes or a coumarone indene resin such as Picco 6100-1-kor Piccotex 100. Distillation, "F The addition of the above plasticizers to the MgO gig dispersions improves the mixing and extrusioncharac- 0% 757 teristics of the dispersion without affecting the disper- 38; g sion performance in neoprene. When the liquid Aniline point up 209 elastomers and coumarone indene resins are employed V Absor tivity at 260 p. 0.9 in combination with other plasticizers, they may be m gg g 23 used at 04-20 parts by weight per hundred parts by Refractivity Intercept 1.0423 i h f M Molecular Analysis, Clay-Gel, %W

As haltenes I 0 The properties of typlcal petroleum o1ls winch are E Compounds 0.3 employed as plasticizers are as follows: Aromatics 15-5 saturates 84.2

Carbon Atom Analysis,% SHELLFLEX 371 Aromatic Carbon Atoms, C A 2 Naphthenic Carbon Atoms, C 44 Paraffinic Carbon Atoms, C P 54 Vlscoslty, SSU/ l00F. 420 ASTM Rubber Extending Oil Type 4 SSU/2l0F. 53.1

Cyclolube Callflux Bearflex 550 LPO 138 4053 2310 Specific gravity F 1. 0217 0. 9070 0. 9573 0. 0053 0. 0230 API gravity 7.0 14. 7 16.3 24.8 21.7 Color, AS'IM 11-1500 1111.0 2. 0 5 3. 0 3. o Viscosity, sus at F 1. 313, 000 2, 500 530 1, 430 Viscosity, sUs at 210 F 415 38.1 so. a so, 0 7s. 0 Pour point, F H0 35 15 20 10 Flash point. C0O, F 465 v 310 425 400 435 Fire point, (10C,0 F 515 370 470 455 500 Aniline point, F 50. 0 168 204.1 105. 4 Mixed aniline polnt, F 05. 8 Average molecular welght. 435 255 411 436 410 Refractive index 20 C 1. 5843 1. 5422 1. 5294 1. 4936 1. 5043 Molecular analysis, ASTM D-2006 (Rustler):

Asphaltenes None None None None None Nitrogen bases 31 2 10 1 2 First acldafilns 22 17 14 4 9 Second acidaffins 38 63 37 26 33 Parafl] ns 9 18 39 69 56 Gel aromatic 91 82 61 31 44 Molecular analysis, ASTM D-2007 (clay-gel):

Asphaltenes None None None None None Polar compounds 28 3 10 1 2 Aromatics 63 77 50 26 40 saturates ll 20 40 73 58 Neutralization No 0.04 0.03 0.04 0.04 0. 03 Viscosity index 1, 14 104 56 43 18 Viscosity-gravity constant. 0. 9067 0. 9520 0.9020 0. 8426 0.8653 gel'illt-lvfi intercept 1. 0748 1. 0548 1. 0526 1. 0444 1. 0463 Percent 0,1 54 as 23 6 10 Percent- CN 7 34 37 40 43 Percent Cp 39 2s 40 54 47 Lbs. wtJgnl 8.6 8.0 7.9 7.5 7.7

The properties of typical mineral oils that are well known as plasticizers are as follows:

It should be noted that the choice of a specific surface active agent is not critical to the practice of the in- ASTM PICCOTEX 100 vention, as long as it be either nonionic or ionic and does not interfere with the neoprene vulcanization. Representative surface active agents include the fol- Softening point, ball-and-ring 100C. lowing: Color, Gardner sca1e(maximum) l 1 5 Specific gravity 1.04 7 7 Pounds per gallon, solid resin 8.67 Compound Gardner viscosity, in toluene at 25C. at 70 solids name Nonionic agents Class n less than I Span 40.... Sorbitan monopalmitate. Sorbitan fatty acid ester. sapmllficatlon "umber, less f l Span 80.... Sorbitan inonooleate Do. Bromine number (electrometnc), Span 85"... Sorbitan trioleate...- Do. l h 1 2O Tween 20... Polyoxyethylene (20). Sorbitan monolaurate.

Tween 40 do Sorbitan nionopalmitate. h 01% Tween 60 do Sorbitan monostearate l Refracnve Index 25cc" Tween 80:: do:: Sorbitan monooleate. Ozone num 0 Renex Polyoxyethylene esters of Polyoxyethylene acids. Flash point, F. 505 mixed fatty and resin Fire point, "F 570 acids.

Tergltol. NPX Nonylphenyl polyglycol ether.

1 Polyoxy ethylene sorbitan fatty acid esters.

PCCO 610O-l Compound Name Class Nonionic Agents Petroleum hydrocarbon resin (produced by the homo Tergilol Linear alcohol polyglycol and copolymerization of dienes and olefins of the ether aliphatic, alicyclic, and monobenzenoid arylalkene Emulpho' VN-43O Polyoxyethylated fatty acid lgepal CO-430 Nonylphenoxypoly types from distilates of cracked petroleum stocks.) (ethyleneoxy) ethanol Ring and Ball Method Representative examples of metallic soaps or fatty acid esters of metals that fall within the scope of the present invention are the stearates, oleates, palmitates, ricinoleates and octoates of Ca, A1, Mg, and Fe. Other metals which may be utilized are Zn, Cd, Ba, Pb, Na, K, Li and Ni. Preferred examples of the metallic soaps are Mg stearate, Ca stearate, Al stearate, Fe distearate and Fe tristearate.

The surface active agents contemplated within the scope of this invention are either nonionic or ionic or mixtures thereof. As illustrative of classes of well known materials one may refer to the following: Nonionic agents Mono and diglycerides,

Sorbitan fatty acid esters,

Polyoxyethylene sorbitan fatty acid esters, Polyoxyethylene sorbitol esters, Polyoxyethylene acids,

Fatty alcohols Polyethylene glycols,

Nonylphenoxypoly (ethleneoxy) ethanols, Fatty acid esters of: glycerol, ethylene glycol, diand polyethylene glycol, propylene glycol, Tetra esters of pentaerythritol and fatty acids, Ionic Agents Alkyl aryl sulfonates Glycerol monostearate Glycerol tristearate Pent-aerythritol tetra- Fatty acid ester of glycerol Fatty acid ester of glycerol Tetra ester of pentaery -thritol and fatty acids stearate Cetyl stearyl alcohol Fatty alcohol Carbowax 4000 Polyethylene glycol For further embodiments of nonionic and ionic agents that may be employed in the practice of this invention, attention is invited to publications such as General Characteristics of Atlas Surfactants (1963) and Detergents and Emulsifiers 1969 Annual, Edited by John W. McCutcheon; the nonionic and ionic agents disclosed therein being incorporated by reference.

Representative examples of combinations of surface active agents, with and without metallic soaps include thefollowing:

(The preferred ratio of the ingredients is indicated in Parenthesis) Span Tween 60 (50/50) Span 80Tween 80 (60/40) Span 80/ Tween 80/Ethylene glycol monostearate (25/25/50) Span 80/ Tween 80/Glycerol monostearate (40/30/30) Span 80Tween 80/Epolene E-l4 (20/15/65) Span 80/ Tween 80/Ca stearate (40/30/30) Span 80/ Tween 80/Carbowax 4000 (40/30/30) Span 80/Ca stearate (60/40) Span 80/ Al stearate (60/40) Igepa1CO-430/Ca stearate (67/33) lgepal CO-430/ Al stearate (67/33) Although the precise reasoning for the highly improved results achieved by the Mg dispersions of this invention is not entirely understood, it is thought that the beneficial effects may be due to the following:

a. Increase in wetting of the Mg0 particles due to the reduction of the interfacial tension at the interface of Mg0 and plasticizer. The advantages of this are: faster wet out of the Mg0 during dispersion preparation, ability to obtain a higher solids content (or a lower viscosity at the same solids content).

b. Increase in the performance (original Mooney scorch and bin age stability) when used in neoprene. This is believed to be due to a reduction of the interfacial tension at the interface of Mg0 and neoprene rubber, making the Mg0 more reactive.

The Mg0 dispersions of the invention may be prepared employing procedures well known in the art. An effective method involves dispersing the Mg0 in the dispersing medium by vigorous mixing. High shear mixing is desirable. The dispersion can be made at room temperature, but elevated temperatures (80 l20 C.) are preferred. It may be noted that particle size reduction of the Mg0 (prior to, after, or during making the dispersion) improves the dispersion performance.

All dispersions used in the following examples were prepared in a double arm sigma blade mixer. The mixer has a working capacity of 0.7 gal. and is jacketed for steam heating. The dispersions were prepared by adding all ingredients except MgO, and mixing with heating until a temperature of l00-105 C. was reached, then the Mg0 was added and mixing was continued at l00l05 C. until complete wetting of the Mg0 by the dispersing medium.

The neoprene compounding was done on a two-roll laboratory rubber mill. The rubber mill has a front roll and a back roll, each six inches in diameter and thirteen inches in length. The front roll is operated at 24 revolutions per minute, and the back roll is operated at 33.6 revolutions per minute. A 7.5 horsepower motor is used to operate the mill. The composition of the neoprene rubber used in the following examples is as follows:

NEOPRENE RUBBER Neoprene GNA I00 parts Stearic acid 0.5 Mg0 powder or dispersion as shown SRF Carbon Black 29 Neozone A (N-phenyl-a-naphthylamine, antioxidant) 2 Zn0 v 5 The rubber is banded on the front roll of the laboratory mill, and the mill is operated until the band is smooth and free of holes. In succession, stearic acid, Mg0 (powder or dispersion), carbon black, Neozine A and Zn0 are added. Each ingredient is added evenly across the rolls and at a uniform rate and is assimilated into the mix before the next ingredient is added. After mixing, the batch is removed from the mill, weighed,

and again placed into the mill. The rolls are set at a 6() distance of 0.030 inches from each other. The stock is passed through the mill six times. During the milling, water having a temperature of 68 F. is passed through the rolls. The stock is then sheeted from the'mill.

Mooney Scorch performance was determined with a Monsanto Mooney Rheometer at 127 C. using a small rotor according to ASTM Test Method DI646-63.

The Neoprene Grade Mg0 used in the following 10 examples is Maglite D No. 3231, a light calcined, high surface activity, magnesium oxide produced by Merck & Co., Inc. It has the following typical properties:

Chemical Analysis Typical Magnesium oxide Mg0 93. I0 I nition loss 4.86 arbon dioxide CO, 0.46 Combined water H,0 4.40 Calcium oxide CaO 0.79 Silicon dioxide Sit), 0.27 Chloride Cl 0. I 7 Sulfate SO, 0.68 Iron oxide Fe, 0, 0.03 Aluminum oxide Al, 0;, 0.10 Manganese Mn 0.0017 Copper Cu 0.0002 Acid insoluble 0.05

Physical Analysis Typical Appearance Clean, white, odorless powder Refractive index 1.64 Specific gravity 3.32 Weight per gallon 2.8 lb./gal. Bulk (loose) 2lpcf Screen analysis Through I00 mesh 100% Through 200 mesh 100% Through 325 mesh 99.5% Primary Particle size, as determined by an electron microscope Average 0.086 micron Distribution 0.00-0.05 micron 20.9 TD 0.05-0.I0 micron 48.8 0.10-0.15 micron 20.2 0.15-0.20 micron 7.1 0.20 0.25 micron 30 Surface area I85 mlgm. Iodine number I35 EXAMPLE I Dispersion Performance Evaluation Dispersions of MgO (Maglite D) in a White Mineral Oil (Ramol-SS) were made using varying amounts of the surface-active agent Span 80.

Increasing the amounts of Span results in an increase in Mg0 wetting as is shown by differences in consistency.

Dispersion Composition Consistency at (weight Room Temperature Maglite Mineral Span D Oil 80 50 50 0 Very dry crumbly paste 50 47.5 2.5 Very dry crumbly paste 50 42.5 7.5 Soft paste 50 37.5 l2.5 Semi-liquid paste ditions to the neoprene compound was judged from Mooney scorch r times. The t is the time required for the Mooney viscosity to increase units above the minimum. Desirably, the t times for Original Mooney Scorch should be relatively long (similar to what results from the use of Maglite D powder at 4 phr). Next, the unvulcanized compounds were aged during 6 days at 50 C., after which the Mooney viscosity t time was determined. Desirably, the t time should change little during bin aging. If the t times of the original or the bin aged compounds are short, then the rubber processor does not have sufficient time to process and v-ulcanize his compounds. This results in scrap. Relatively high 2 times reduce losses due to scrap and allow less critical conditions for processing and storage of the unvulcanized neoprene compounds.

A comparison of the Mooney Scorch Protection of the above dispersion compositions of the invention (A) V (b-d) which contain 2 phr (4 phr X 50 percent) of Maglite D and Maglite D powder (B) at the 2 phr level clearly reveals the beneficial effects produced by the dispersions of the invention. In fact the dispersion of the invention containing 2 phr of Maglite D (A) (d) is decidedly superior to prior art Maglite D powder at the 4 phr level. It should also be noted that the dispersion compositions of the invention (A) (b-d) are distinctly better than the prior art dispersion of Maglite D in mineral oil (A) (a).

Comparable results to those reported above were achieved when other MgO dispersions within the scope of the invention such as the following were tested with respect to their ability to protect against scorch:

Dispersion composition (weight percent) Surface-active agent or metallic Consistency at room Maglite D Plasticizer soap temperature 50 Mineral oil (Hamel-85) (50%) None Very dry, crumbly paste. 50. Mineral Oil (Raml-85) (42.5 Epolene E-14 (75%)-- Soft paste.

50. Petroleum oil, aromatic (Bearfiex-LPO) (45%).. Renex (5%) Do.

50 do Atlas G3300 (5%) Very soft paste. 60. do Glycerol monostearate (6%). Soft paste.

50-.- ..do Igepal C 0 (5 Semi-liquid paste 50--. .do Ganex V-216 (5% Soft paste.

50 o Emulphor VN-430 (5%) Very soft piste 50-- Kenflex N (45%). Ethyleneglycol monostearate (5%) Soft paste.

50. Butyl oleate (45 Cetyl stearyl alcohol (5%) Stifi paste.

5() Dibutyl phthalate (45%) Span 80 (5%) Soft paste.

50. Tricresyi phosphate (45% do Do.

60. Petroleum oil, aromatic (Bearflex-LPO) (32%).- Ferric distearate (8%) Do.

EXAMPLE II The beneficial effects on Mooney Scorch, original as well as after bin aging are demonstrated by representative dispersions of the invention. The tests were carried The following 50 percent dispersions were used at 4 35 out in accordance with the Dispersion Performance phr in neoprene:

Evaluation discussed above.

Original and bin age Mooney scorch protection t e time Dispersion composition (weight percent) (minutes) After 6 days at Maglite D Plasticizer Surface active agent Original 50 C.

50. Mineral oil (Rarnol-85) (42.5%) Epolcne E-l4 (7.5%) 43 30 50 Petroleum oil aromatic (Bearflex-LPO) (45%) Atlas G-3300 (5%) 42 33 .do Glycerol monostearate (5%) 39 32 50... ..do Emulphor VN-430 42 32 50 enfiex N (45%) Ethyleneglycol monosteatate (5%) 44 31 g p i i ofi l d A The following is a comparison between a representag fgfi 51; Z ;{,,,f 50 tive prior art MgO dispersion and a dispersion of i time (minutes) Maglite D within the scope of the invention. g M M The prior art dispersion is a soft plastic form which Magma 33 or'gml 5 oo utilizes aliphatic materials as the dispersing medium for the MgO. (a) 50 50 0 42 28 55 Dispersion of Maglite D has the following composition: (b) 50 47.5 2.5 45 30 (c) 50 42.5 7.5 44 35 ((1)50 37.5 12.5 45 38 Maglite D 52.9%

Petroleum Oil, Naphtlienic Maglite D powder was slmilarly used at the levels 1- (Shellflex 371) 43.3 s so 2 4 drcated: pan v Calcium stearate 1.4

(B) Maglite D (phr) Original & Bin Age Mooney Scorch Protection I time (minutes) Original at 50C. 4 40 35 2 34 23 After 6 days Original and Bin Age Mooney Scorch Protection 2 time (minutes) Original After 6 days Dispersion of Maglite D This experiment clearly demonstrates that the MgO dispersions of the invention are markedly superior over the prior art dipersions.

Additional examples of representative formulations that may be employed in the practice of the invention are as follows:

In the above formulations highly desirable results are obtained by replacing 2 parts of oil with 2 parts of coumarone indene resin (e.g., Piccotex 100 or Picco 6l001- /z) or 2 parts of liquid elastomer (e.g., Vistanex LM-MS).

MgO 53.0 Shellflex 371 41.2 Piccotex I 2.0 Al Stearate l.4 Polyoxyethylene sorbitan monooleate 2.4

Preparation of Stick Form of MgO dispersion After the dispersion is prepared by high shear mixing, the hot dispersion is extruded through a hot extruder. The extruded stick is then cut into the desired lengths, and cooled to room temperature.

Preparation of Pellet Form of MgO Dispersion Pellets are prepared by adding the hot dispersing medium to the powder while it is being mixed slowly at abut 100C. Just enough dispersing medium is added to make the particles coalesce.

When certain representative embodiments and details have been shown for the purpose of illustrating the invention it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing from the spirit or scope of the invention.

What is claimed is:

l. A chloroprene polymer containing a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total mount of surface active agent being from about 2.5 to about 50 parts based upon per hundred parts by weight of M g0, and the amount of rubber plasticizer is from about 5 to about based upon per hundred parts by weight of MgO.

2. The chloroprene polymer according to claim 1 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.

3. The chloroprene polymer according to claim 2 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate ofCa, Al, Mg, or Fe.

' 4. The chloroprene polymer according to claim 3 wherein the rubber plasticizer is a petroleum oil.

5. The chloroprene polymer of claim 4 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.

6. The chloroprene polymer according to claim 5 which further contains a coumarone indene resin.

7. The chloroprene polymer of claim 4 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.

8. The chloroprene polymer according to claim 7 which further contains a coumarone indene resin.

9. The chloroprene polymer according to claim 7 which further contains polyisobutylene.

10. The chloroprene polymer according to claim 4 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra stearate.

11. In the method of utilizing MgO in the compounding and processing of chloroprene polymers, the improvement comprising employing a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 parts by weight based upon per hundred parts by weight of MgO.

12. The method according to claim 11 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.

13. The method according to claim 12 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate ofCa, Al, Mg, or Fe.

14. The method according to claim 13 wherein the rubber plasticizer is a petroleum oil.

15. The method according to claim 14 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.

16. The method according to claim 14 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra-stearate.

17. The method of claim 14 wherein the surface active agent is nonylphenoxypoly (ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.

18. The method according to claim 17 which further contains a coumarone indene resin.

19. The method according to claim 15 wherein the dispersion further contains a coumarone indene resin.

20. The method according to claim 15 wherein the dispersion further contains polyisobutylene.

21. A composition for use in the compounding and processing to chloroprene polymers comprising a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about to about 70 parts by weight based upon per hundred parts by weight of MgO.

22. The composition of claim 21 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.

23. The composition of claim 22 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg, or Fe.

24. The composition of claim 23 wherein the rubber plasticizer is a petroleum oil.

25. The composition of claim 24 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.

26. The composition of claim 25 which further contains a coumarone indene resin.

27. The composition of claim 25 which further contains polyisobutylene.

28. The composition of claim 24 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.

29. The composition of claim 28 which further contains a coumarone indene resin.

30. The composition according to claim 24 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetrastearate.

31. A process of producing a vulcanizable chloroprene polymer which comprises the addition of a dispersion of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about parts by weight based upon per hundred parts by weight of MgO to a composition comprising chloroprene.

32. The process according to claim 31 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.

33. The process according to claim 32 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly(ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate ofCa, Al, Mg, or Fe.

34. The process according to claim 32 wherein the rubber plasticizer is a petroleum oil.

35. The process of claim 34 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.

36. The process according to claim 34 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra-stearate.

37. The process of claim 35 wherein the dispersible form of MgO further contains a coumarone indene resin.

38. The process of claim 35 wherein the dispersible form of MgO further contains polyisobutylene.

39. The process according to claim 34 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.

40. The process according to claim 39 which further contains a coumarone indene resin.

41. A stick or pcllct for the use in the compounding and processing of chloroprene polymers cmnprisiny, a

dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixture thereof and at least one rubber plasticizer, the total amount of surface active agent being from about 2.5 to about 50 par-ts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about to about 70 parts by weight based upon per hundred parts by weight of MgO.

42. The stick or pellet according to claim 41 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly(ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.

43 The stick or pellet according to claim 42 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly(ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg or Fe.

44. The stick or pellet according to claim 43 wherein the rubber plasticizer is a petroleum oil.

45. The stick or pellet according to claim 44 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.

46. The stick or pellet according to claim 44 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.

47. The stick or pellet according to claim 46 which further contains a coumarone indene resin.

Disclaimer 3,717,600.AZbert J. Dalhm'sen, Sunnyvale, William H. Debs, Belmont, and

Dwvz'd 0'. B'wgett, Daly City, Calif. MAGNESIUM OXIDE DIS- PERSIONS. Patent dated Feb. 20, 1973. Disclaimer filed Mar. 14, 1977, by the assignee, Mewck c@ 00., Inc. Hereby enters this disclaimer to claims 1-47 of said patent.

[OfiZOiaZ Gazette May 10, 1977.]

Disclaimer 3,717,600.AZbert J. Dalhm'sen, Sunnyvale, William H. Debit, Belmont, and

David 0. Burgett, Daly City, Calif. MAGNESIUM OXIDE DIS- PERSIONS. Patent dated Feb. 20, 1973. Disclaimer filed Mar. 14, 1977, by the assignee, Merck c@ 00., Inc. Hereby enters this disclaimer to claims 1-47 of said patent.

[Ofiicial Gazette May 10, 1,977.] 

1. A chloroprene polymer containing a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total mount of surface active agent being from about 2.5 to about 50 parts based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 based upon per hundred parts by weight of MgO.
 2. The chloroprene polymer according to claim 1 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.
 3. The chloroprene polymer according to claim 2 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg, or Fe.
 4. The chloroprene polymer according to claim 3 wherein the rubber plasticizer is a petroleum oil.
 5. The chloroprene polymer of claim 4 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.
 6. The chloroprene polymer according to claim 5 which further contains a coumarone indene resin.
 7. The chloroprene polymer of claim 4 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.
 8. The chloroprene polymer according to claim 7 which further contains a coumarone indene resin.
 9. The chloroprene polymer according to claim 7 which further contains polyisobutylene.
 10. The chloroprene polymer according to claim 4 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra stearate.
 11. In the method of utilizing MgO in the compounding and processing of chloroprene polymers, the improvement comprising employing a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 parts by weight based upon per hundred parts by weight of MgO.
 12. The method according to claim 11 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.
 13. The method according to claim 12 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg, or Fe.
 14. The method according to claim 13 wherein the rubber plasticizer is a petroleum oil.
 15. The method according to claim 14 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.
 16. The method according to claim 14 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra-stearate.
 17. The method of claim 14 wherein the surface active agent is nonylphenoxypoly (ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.
 18. The method according to claim 17 which further contains a coumarone indene resin.
 19. The method according to claim 15 wherein the dispersion further contains a coumarone indene resin.
 20. The method according to claim 15 wherein the dispersion further contains polyisobutylene.
 21. A composition for use in the compounding and processing to chloroprene polymers comprising a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 parts by weight based upon per hundred parts by weight of MgO.
 22. The composition of claim 21 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, pOlyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.
 23. The composition of claim 22 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly (ethyleneoxy) ethanols and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg, or Fe.
 24. The composition of claim 23 wherein the rubber plasticizer is a petroleum oil.
 25. The composition of claim 24 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.
 26. The composition of claim 25 which further contains a coumarone indene resin.
 27. The composition of claim 25 which further contains polyisobutylene.
 28. The composition of claim 24 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.
 29. The composition of claim 28 which further contains a coumarone indene resin.
 30. The composition according to claim 24 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra-stearate.
 31. A process of producing a vulcanizable chloroprene polymer which comprises the addition of a dispersion of MgO and at least one ionic or nonionic surface active agent or mixtures thereof and at least one rubber plasticizer wherein there is from about 2 to about 16 parts of a dispersion of MgO by weight per hundred parts by weight of polymer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 parts by weight based upon per hundred parts by weight of MgO to a composition comprising chloroprene.
 32. The process according to claim 31 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly (ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap.
 33. The process according to claim 32 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxypoly(ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg, or Fe.
 34. The process according to claim 32 wherein the rubber plasticizer is a petroleum oil.
 35. The process of claim 34 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.
 36. The process according to claim 34 wherein the rubber plasticizer is a naphthenic petroleum oil and the surface active agent is pentaerythritol tetra-stearate.
 37. The process of claim 35 wherein the dispersible form of MgO further contains a coumarone indene resin.
 38. The process of claim 35 wherein the dispersible form of MgO further contains polyisobutylene.
 39. The process according to claim 34 wherein the surface active agent is nonylphenoxypoly(ethyleneoxy) ethanol, the rubber plasticizer is a naphthenic petroleum oil and the metallic soap is calcium stearate.
 40. The process according to claim 39 which further contains a coumarone indene resin.
 41. A stick or pellet for the use in the compounding anD processing of chloroprene polymers comprising a dispersion of MgO which is comprised of MgO and at least one ionic or nonionic surface active agent or mixture thereof and at least one rubber plasticizer, the total amount of surface active agent being from about 2.5 to about 50 parts by weight based upon per hundred parts by weight of MgO, and the amount of rubber plasticizer is from about 5 to about 70 parts by weight based upon per hundred parts by weight of MgO.
 42. The stick or pellet according to claim 41 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol esters, polyoxyethylene acids, fatty alcohols, polyethylene glycols, nonylphenoxypoly(ethyleneoxy) ethanols, fatty acid esters of glycerol, ethylene glycol, polyethylene glycol or propylene glycol, and tetra esters of pentaerythritol and fatty acids and the ionic surface active agent is an alkyl aryl sulfonate or a metallic soap. 43 The stick or pellet according to claim 42 wherein the nonionic surface active agent is selected from the group consisting of sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, nonylphenoxy-poly(ethyleneoxy) ethanols, and tetra ester of pentaerythritol and fatty acids and the metallic soap is a stearate of Ca, Al, Mg or Fe.
 44. The stick or pellet according to claim 43 wherein the rubber plasticizer is a petroleum oil.
 45. The stick or pellet according to claim 44 wherein the rubber plasticizer is a naphthenic petroleum oil, the surface active agent is sorbitan monooleate and the metallic soap is calcium stearate.